Grades

Ferro Titanium 60% to 75% is a low residual, low melting point titanium alloy consumed in the steel industry. Ferro Titanium is produced using titanium scrap and low carbon iron scrap.

The scrap blend is such that 60% to 75% Titanium content is contained in the final product. At this ratio of titanium iron, a eutectic is achieved in which the melting point of the alloy is 1,200°C whereas Titanium & Iron melt at approx, 650°C. This eutectic allows rapid dissolution of the alloy.

Different grades of steel require demand different chemical compositions of Ferro Titanium. At M/s Bansal Brothers we expertise in controlling all the material elements in the alloy. Below is a chart of the various grades of Ferro Titanium offered by Ferro Alloys Division of M/s Bansal Brothers.

Chemical Composition of various grades of Ferro Titanium Products offered

Grade TI %age AL %age V %age C %age SI %age P %age S %age CU %age MN %age O %age N %age
70% STD I Min 68 0 0 0 0 0 0 0 N/A N/A N/A
Max 72 5 3 0.2 0.5 0.05 0.05 0.2
70% STD Low N Min 68 0 0 0 0 0 0 0 N/A N/A 0
Max 72 5 3 0.2 0.5 0.05 0.05 0.2 0.4
70% Low Al 3 Min 65 0 N/A 0 0 0 0 0 N/A N/A N/A
Max 70 3 0.15 0.5 0.04 0.03 0.04
70% Low Mn 1 Min 68 0 N/A 0 0 0 0 0 0 N/A N/A
Max 72 5 0.2 4 0.06 0.03 0.04 1
70% Low Al 1 Min 65 0 0 N/A 0 0 0 0 N/A N/A N/A
Max 67 1 0.15 0.5 0.05 0.05
70% Low C Min 68 0 0 0 0 0 0 N/A N/A N/A N/A
Max 72 5 4 0.1 3 0.05 0.05
30% Low C Min 25 0 0 0 0 0 0 N/A N/A N/A N/A
Max 30 6 5 0.1 3 0.05 0.05
30% Low N Min 25 0 0 0 0 0 0 N/A N/A N/A 0
Max 30 6 5 0.1 3 0.05 0.05 0.4
30% STD Min 25 0 0 0 0 0 0 N/A N/A N/A N/A
Max 30 6 5 0.2 5 0.05 0.05

We can provide special grades of Ferro Titanum with low Carbon and low Aluminium wherein Carbon is max. 0.1% and Aluminium is max 5%. We have capability to control Oxygen and Nitrogen levels as per customer's specifications. Titanium content can be customized between 30% and 75%. We also customize the chemical composition of Ferro Titanium alloy to cater to any special alloying needs of our customers. This is mainly done by preparing a researched & customized raw material recipe and altering the heat time of the specific batches.